T130-52

A_L value (nominal)

79 nH/ N²

μi (reference)

µ 75

Density gm/cm³

7.0

Test Winding          

N=10, #24 AWG

Frequency              

10 kHz

Voltage on Agilent 4284A

0.31  V

Coating Type

Green/Blue Epoxy Paint

Voltage Breakdown (min.)

500 Vrms, 60Hz

Limit

0.1 mA, 5 s

Magnetic

Dimensions

L_e Eff. Mag. Path Length (cm)

A_e

Eff. Mag. Cross Section (cm²)

V_eff Eff. Core Volume (cm³)

WA - Min. Eff. Window Area

sa - Surface Area

mlt - mean length per turn

8.28 cm

0.698 cm²

5.78 cm³

2.93 cm²

39.8 cm²

4.73 cm

Core Loss

Bpk

140 G

Frequenzy

100 kHz

Core Loss (nominal)

58 mW/cm³

Core Loss (maximum)

67 mW/cm³

where Bpk expressed in gauss, f expressed in hertz, and:

a=1.00E+09, b=1.10E+08, c=2.10E+06, d=6.90E-14

DC Saturation

HDC

Percent Initial Perm (nom.)

Percent Initial Perm (min.)

50 Oe

61.6%

53.4%

where H expressed in oersteds, and:

a=1.00E-02, b=4.66E-06, c=1.84, d=0.00

AWG

8

10

12

14

16

18

20

22

24

26

28

mm

3.150

2.500

2000

1.600

1.250

1000

0.800

0.630

0.500

0.400

0.315

Turns

14

18

22

29

36

46

58

73

91

114

142

RDC(Ω)

1.4 m

2.8 m

5.4 m

11.4 m

22.4 m

45.6 m

91.4 m

182.9 m

362.6 m

722.4 m

1.4

Turns

15

24

37

57

88

136

211

326

504

781

1.208

RDC(Ω)

1.5 m

3.7 m

9.1 m

22.3 m

54.8 m

134.7 m

332.4 m

816.7 m

2.0

4.9

12.2