T106-0

A_L value (nominal)

1.9 nH/ N²

μi (reference)

µ 1

Density gm/cm³

N/A

Test Winding          

N=100, #28 AWG

Frequency              

10 kHz

Voltage on Agilent 4284A

0.12  V

Coating Type

Tan/Tan Epoxy Paint

Voltage Breakdown (min.)

500 Vrms, 60Hz

Limit

0.1 mA, 5 s

Magnetic

Dimensions

L_e Eff. Mag. Path Length (cm)

A_e

Eff. Mag. Cross Section (cm²)

V_eff Eff. Core Volume (cm³)

WA - Min. Eff. Window Area

sa - Surface Area

mlt - mean length per turn

6.49 cm

0.659 cm²

4.28 cm³

1.53 cm²

28.1 cm²

4.39 cm

Core Loss

Bpk

140 G

Frequenzy

100 kHz

Core Loss (nominal)

0 mW/cm³

Core Loss (maximum)

0 mW/cm³

where Bpk expressed in gauss, f expressed in hertz, and:

a=1.00E+99, b=1.00E+99, c=1.00E+99, d=0.00E+00

DC Saturation

H_dc

Percent Initial Perm (nom.)

Percent Initial Perm (min.)

200 Oe

100.0%

100.0%

where H expressed in oersteds, and:

a=1.00E-02, b=0.00E+00, c=0.00, d=0.00

AWG

10

12

14

16

18

20

22

24

26

28

30

mm

2.500

2.000

1.600

1.250

1.000

0.800

0.630

0.500

0.400

0.315

0.250

Turns

12

15

20

26

32

41

52

65

82

102

128

RDC(Ω)

1.7 m

3.4 m

7.3 m

15.0 m

29.4 m

59.9 m

120.8 m

240.2 m

482.0 m

953.5 m

1.9

Turns

12

19

30

46

71

110

171

264

409

633

980

RDC(Ω)

1.7 m

4.3 m

10.9 m

26.6 m

65.2 m

160.7 m

397.4 m

975.7 m

2.4

5.9

14.6