T200-13

Kern

Farbe

Außen

mm

Innen

mm

Höhe

mm

Perme-abilität

A_L (nH/100Wdgg.²)

A_L-Toleranz

Frequenz-bereich

Mass

(approximate)

T200-13

Grau

50.80

31.75

13.97

µ 35

425

±10%

0.05-0.5 MHz

110

gramm

A_L value (nominal)

42.5 nH/ N²

µ_i (reference)

µ 35

Density gm/cm³

6.5

Test Winding          

N=100, #20 AWG

Frequency              

10 KHz

Voltage on Agilent 4284A

0.56 V

Coating Type

Grau/Clear Epoxy Paint

Voltage Breakdown (min.)

500 Vrms, 60Hz

Limit

0.1 mA, 5 s

Magnetic

Dimensions

L_e Eff. Mag. Path Length (cm)

A_e

Eff. Mag. Cross Section (cm²)

V_eff Eff. Core Volume (cm³)

WA - Min. Eff. Window Area

sa - Surface Area

mlt - mean length per turn

13.0 cm

1.27 cm²

16.4 cm³

7.60 cm²

88.4 cm²

6.53 cm

Core Loss

Bpk

140

Frequenzy

100 kHz

Core Loss (nominal)

31 mW/cm³

Core Loss (maximum)

36 mW/cm³

where Bpk expressed in gauss, f expressed in hertz, and:

a=1.90E+09, b=2.00E+08, c=9.00E+05, d=4.30E-15

DC Saturation

H_dc

Percent Initial Perm (nom.)

Percent Initial Perm (min.)

200 Oe

60.1%

53.7%

where H expressed in oersteds, and:

a=1.00E-02, b=4.87E-08, c=1.57, d=0.00

Wire Size

AWG

8

10

12

14

16

18

20

22

24

26

28

mm

3.150

2.500

2000

1.600

1.250

1000

0.800

0.630

0.500

0.400

0.315

Single Layer

Turns

24

30

38

48

60

76

95

119

149

185

231

RDC(Ω)

3.2 m

6.4 m

12.9 m

25.9 m

51.6 m

103.9 m

206.5 m

411.4 m

819.3 m

1.6

3.2

Full Winding

Turns

40

62

95

148

228

353

547

847

1,311

2,029

3,140

RDC(Ω)

5.4 m

13.2 m

32.2 m

80.0 m

196.0 m

482.5 m

1.2 m

2.9

7,2

17.7

43.7